15-7 Mo Stainless steel

15-7 Mo Stainless steel 
                                 
Equal material :S15700，SUS632，X8CrNiMoAI15-7-2，1.4532

JOIN WIN STEEL 15-7 Mo provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective balance of properties by simple heat treatment. 15-7 Mo alloy is useful for a wide range of applications that include retaining rings, springs, diaphragms, aircraft bulkheads, welded and brazed honeycomb paneling and other aircraft components requiring high strength at elevated temperatures.

The material supplied from the mill is in Condition A. After fabrication, and conditioning treatments, the material is precipitation hardened into either Condition TH 1050 or Condition RH 950. To achieve the highest mechanical properties Condition A material is transformed to martensite at the mill by cold reduction to Condition C. After fabrication by the user a single low-temperature heat treatment is preformed to achieve condition CH 900.

Email  william(at)steel-jw(dot)com

Skype william.join-win

Url www(dot)c267steel(dot)com

www(dot)x80pipeline(dot)com

www(dot)steel-jw(dot)com

Tel 86,371,63332179

来自 “ ITPUB博客 ” ，链接：http://blog.itpub.net/29531879/viewspace-1143046/，如需转载，请注明出处，否则将追究法律责任。

转载于:http://blog.itpub.net/29531879/viewspace-1143046/